POLIKES® -  PA6 G (CAST POLYAMIDE) It is a plastic with high physical, electrical and chemical resistance.  Its resistance is high especially against strokes and loads. Its temperature resistance is high, whereas corrosion coefficient is low. But, because of its water absorption property, it is not recommended at humid environments(%6-7). PROPERTIES OF POLIKES® · 100°C Service Temperature · Low Corrosion Coefficient · Very High Pressing Resistance · High Hardness · High Resistance To Strokes · Resistance To Heat · Resistance To Chemical Substances · Lower Water Absorption compared to PA 6   GENERAL USAGE AREAS OF POLIKES® . Sledges . Wheels . Rolls . Gears . Bearings . Bobbins . Hoops . Corrosion Plates . Food Industry Parts . Chemical Industry Parts . Paper Industry Parts . Textile Industry Parts . Press Industry Parts POLIKES® PRODUCTS · WEDGES · PLATES POLIKES® (PA6 G) CHEMICAL RESISTANCE TABLE   50% Acetone + Pure Acetone (+) Formic acid 10% - Ammonia 10% + Anone + 96% Ethanole + Acetone Ethele + Other Etheles + Ethylene Chloride + Benzole + Benzene + Tar (+) Boric acid Solution 10% + Buthyl Acetate + Calcium Chloride 10% + Chlorbenzene + Chloraform - Citric Acid Solution (+) Chlophene A60 50% + Cyclohexane + Cyclohexanone + Decaline + Motor Oil + Dimethyle Formamide + Dioctyl Phthalato + Dioxane + Acetic Acid Concentration - Acetic Acid Solution 10% - Acetic Acid Solution 5% + Hydrofluoric Acid - Formaldeid 30% + Formamide + Liquid Freon + Fruit Juice + Gyeol + Gysantin, Aqueous solution 40% + Gycerine + Urea + Warm Oil + Hegzane + Iso - Octane + Isopropanol + Lodine Solution, Alcohol Solution - Potassium Solution 50% + Potassium Solution 10% + Potassium dich.squacus sol. 10% + Potassium perm. Squacus sol. 1% - Cupric Sulphate 10% + Linseed Oil + Methanole + Molthyl Ethyle Cetone + Molthylene Chloride (+) Milk + Lactic Acid 90% - Lactic Acid 10% + Sodium Bisulphite Aqueous 10% + Sodium Carbonate + Sodium Chloride + Sodium Nitrate + Sodium Sulphate + Mineral Solution 50% + Mineral Solution 5% + Nitrobenzene (+) Oxalic Acid Solution 10% (+) Ozone - Paraffin Oil + Perchioroethylene (+) Raw Petroleum + Pfenol Solution - Concentrated Phosphoricacid - Phosphoricacid 10% - Phenole + Pyridine + Pyridine 3 Solution, Aqueous Sol. + Salycic Acid + Nitric Acid, Aqueous Sol. 2% - Hydrochloric Acid, Aqueous Sol. 38% - Hydrochloric Acid, Aqueous Sol. 2% - Oxide + Sulphuric Acid Concentrate 98% - Sulphuric acid 2% - Hydrogen Sulphide, Saturated + Soap Solution, Aqueous Solution + Slycone Oil + Mineral Solutions, Aqueous Sol. 10% + Ediple Fats, Ediple Oils + Styrane + Tar (+) Carbon Tetrachloride + Tetrahydrofurane + Tetraline + Ink + Toluene + Transfer Oil + Triethanolamine + Trichlorethylene (+) Trilon B, Aqueous Solution 10% + Vaseline + Wax, Molten + Cold Water + Tepid Water (+) Hydrogen Per. , Aqueous Sol. 30% - Hydrogen Peroxide, Aqu. Sol. 5% - Wine, Brandy + Tartaric Acid + Xylene + Zinc Chloride, Aqueous Sol. 10% (+) PHYSICAL PROPERTIES OF POLIKES®    PROPERTIES UNIT TEST METHOD VALUE  DN ISO SPECIFIC GRAVITY g/cm3 53479 1183  1,15 SERVICE TEMPERATURE 0 °C  53461 75 100  MELTING POINT 0 °C  -  - 190 THERMAL ELONGATION 1/K*105  53752  -  8-9 PULLING RESISTANCE N/mm2  53455 527  55-85 PULLING ELONGATION %  53455 527  - BREAKING RESISTANCE N/mm5  53455 527  88-90 BREAKING ELONGATION %  53455 527  10-40 STROKE RESISTANCE Kj/m2 53453 179  - NOTCH STROKE RESISTANCE kj/m2  Kj/m2  53453 179  - ELASTIC MODULE N/mm2  53452 178  3900-4200 WATER ABSORPTION %  53495 62  6-7 RESISTANCE AS PER VOLUME   W x cm  53482 167  >1015 RESISTANCE AS PER SURFACE W  53482 167  >1012 DIELECTRIC RESISTANCE KV/mm  53481 243  80-100 CORROSION (SAND SLURRY TEST) %  58836 -  - SHORE Skala D  53505    85 ROCKWELL Skala  -  2039-2  M88 BALL NOTCH 358/30 N/mm2  53456  2039-1  110-160